Studi Perbandingan Kinerja Anoda Korban Paduan Aluminium dengan Paduan Seng dalam Lingkungan Air Laut

Abstract

There are two kinds of sacrificial anodes available to protect steel structure in the marine environment; they are zinc and aluminum alloy. This research studies their performance by conducting galvanic corrosion test in the substitute ocean water. The performance evaluated covers potential of protection, galvanic current, capacity and efficiency, the rate of anode consumption, the induction time, and their corrosion form.
The result shows that aluminum alloy has galvanic current and anode capacity higher than the zinc alloy. It is also found that this alloy gives the higher efficiency and shows the lower anode consumption rate than the zinc alloy. From the macro photographs, it is found that these two alloys corrode locally by pitting formation. Abstract in Bahasa Indonesia : Terdapat dua jenis paduan anoda korban yang digunakan untuk memproteksi struktur baja karbon di lingkungan air laut, yaitu paduan aluminium dan paduan seng. Penelitian ini bertujuan mempelajari kinerja dua jenis anoda korban tersebut dengan melakukan uji korosi galvanik dalam lingkungan pengganti air laut. Kinerja yang diukur adalah potensial proteksi, arus galvanik, kapasitas anoda, efisiensi anoda, laju konsumsi anoda, waktu induksi, dan pola korosi anoda.
Hasil penelitian menunjukkan anoda korban paduan aluminium menghasilkan arus galvanik dan kapasitas anoda yang lebih besar daripada paduan seng. Demikian pula efisiensi paduan aluminium lebih baik dan laju konsumsinya lebih rendah daripada paduan seng. Dengan foto makro tampak bahwa pola korosi yang terjadi pada kedua jenis paduan menunjukkan anoda korban tidak terkorosi secara merata, melainkan terjadinya korosi pitting pada permukaannya. Kata kunci : proteksi katodik, anoda korban, lingkungan pengganti air laut.