Struktur Mikro Las Baja C-Mn Hasil Pengelasan Busur Terendam dengan Variasi Masukan Panas

Abstract

This research aims to study the effect of heat input of submerged arc welding on the microstructure of weld metal made from C-Mn steel. The study focused on the formation of acicular ferrite which could improve weld mechanical properties. The welding process was carried out using various heat inputs, i.e. 3.99 kJ/mm, 3.19 kJ/mm, 2.12 kJ/mm, and 1.77 kJ/mm. Microstructural examinations were performed using optical microscope and scanning electron microscope (SEM). Results show that the weld metal welded with heat input 2.12 kJ/mm produces more acicular ferrite than grain boundary and Widmanstatten ferrite. It is evident that this acicular ferrite nucleates on inclusions in the forms of SiO₂, TiO, and Al₂O₃. Abstract in Bahasa Indoensia: Penelitian ini bertujuan untuk mempelajari pengaruh masukan panas proses las busur rendam pada struktur mikro logam las baja C-Mn. Struktur mikro dengan bentuk acicular ferrite merupakan struktur yang dapat meningkatkan sifat mekanis logam las. Proses pengelasan yang digunakan dalam penelitian ini menggunakan empat macam masukan panas yang berbeda, yaitu 3,99 kJ/mm, 3,19 kJ/mm, 2,12 kJ/mm, dan 1,77 kJ/mm. Struktur mikro yang terbentuk diuji dengan mikroskop optik dan scanning electron microscope (SEM). Hasilnya menunjukkan bahwa logam las dengan masukan panas 2,12 kJ/mm mempunyai jumlah struktur acicular ferrite lebih besar dari pada grain boundary ferrite dan widmanstatten ferrite. Hal ini disebabkan oleh adanya nukleasi dari inklusi yang berbentuk SiO₂, TiO, dan Al₂O₃. Kata kunci: masukan panas, acicular ferrite, sifat mekanis